Crystalline Phases Involved in the Hydration of Calcium Silicate‐Based Cements: Semi‐Quantitative Rietveld X‐Ray Diffraction Analysis


Chemical comparisons of powder and hydrated forms of calcium silicate cements (CSCs) and calculation of alterations in tricalcium silicate (Ca3SiO5) calcium hydroxide (Ca(OH)2) are essential for understanding their hydration processes. This study aimed to evaluate and compare these changes in ProRoot MTA, Biodentine and CEM cement. Powder and hydrated forms of tooth coloured ProRoot MTA, Biodentine and CEM cement were subjected to X-ray diffraction (XRD) analysis with Rietveld refinement to semi-quantitatively identify and quantify the main phases involved in their hydration process. Data were reported descriptively. Reduction in Ca3SiO5 and formation of Ca(OH)2 were seen after the hydration of ProRoot MTA and Biodentine; however, in the case of CEM cement, no reduction of Ca3SiO5 and no formation of Ca(OH)2 were detected. The highest percentages of amorphous phases were seen in Biodentine samples. Ettringite was detected in the hydrated forms of ProRoot MTA and CEM cement but not in Biodentine.

Keywords: X-Ray Diffraction Analysis, Chemical Properties, Mineral Trioxide Aggregate
  To share this page with others, use links below: